Combined plasma gas-phase synthesis and colloidal processing of inp/zns core/shell nanocrystals

Ryan Gresback, Ryan Hue, Wayne L. Gladfelter, Uwe R. Kortshagen

Research output: Contribution to journalArticlepeer-review

19 Scopus citations


Indium phosphide nanocrystals (InP NCs) with diameters ranging from 2 to 5 nm were synthesized with a scalable, flow-through, nonthermal plasma process at a rate ranging from 10 to 40 mg/h. The NC size is controlled through the plasma operating parameters, with the residence time of the gas in the plasma region strongly influencing the NC size. The NC size distribution is narrow with the standard deviation being less than 20% of the mean NC size. Zinc sulfide (ZnS) shells were grown around the plasma-synthesized InP NCs in a liquid phase reaction. Photoluminescence with quantum yields as high as 15% were observed for the InP/ZnS core-shell NCs.

Original languageEnglish (US)
Article number68
JournalNanoscale Research Letters
Issue number1
StatePublished - Jan 2011

Bibliographical note

Funding Information:
This study was supported primarily by the MRSEC Program of the National Science Foundation under Award Number DMR-0819885. Partial support through the University of Minnesota Center for Nanostructure Applications is acknowledged. The authors utilized the University of Minnesota Characterization Facility which receives partial support from the NSF under the NNIN program.


Dive into the research topics of 'Combined plasma gas-phase synthesis and colloidal processing of inp/zns core/shell nanocrystals'. Together they form a unique fingerprint.

Cite this