High Ms Fe16N2 thin film with Ag under layer on GaAs substrate

Xiaowei Zhang, Yanfeng Jiang, Meiyin Yang, Lawrence F. Allard, Jian Ping Wang

Research output: Contribution to journalArticlepeer-review

Abstract

(001) textured Fe16N2 thin film with Ag under layer is successfully grown on GaAs substrate using a facing target sputtering (FTS) system. After post annealing, chemically ordered Fe16N2 phase is formed and detected by X-ray diffraction (XRD). High saturation magnetization (Ms) is measured by a vibrating sample magnetometer (VSM). In comparison with Fe16N2 with Ag under layer on MgO substrate and Fe16N2 with Fe under layer on GaAs substrate, the current layer structure shows a higher Ms value, with a magnetically softer feature in contrast to the above cases. In addition, X-ray photoelectron spectroscopy (XPS) is performed to characterize the binding energy of N atoms. To verify the role of strain that the FeN layer experiences in the above three structures, Grazing Incidence X-ray Diffraction (GIXRD) is conducted to reveal a large in-plane lattice constant due to the in-plane biaxial tensile strain.

Original languageEnglish (US)
Article number056203
JournalAIP Advances
Volume6
Issue number5
DOIs
StatePublished - May 1 2016

Fingerprint

Dive into the research topics of 'High Ms Fe<sub>16</sub>N<sub>2</sub> thin film with Ag under layer on GaAs substrate'. Together they form a unique fingerprint.

Cite this