Large strain deformation of bimodal layer thickness Cu/Nb nanolamellar composites

T. A. Wynn, D. Bhattacharyya, D. L. Hammon, A. Misra, N. A. Mara

Research output: Contribution to journalArticlepeer-review

11 Scopus citations

Abstract

Nanolayered composites have garnered much attention due to their ability to withstand deformation to large strains, shock deformation, and irradiation induced microstructural damage. These behaviors have been attributed to high densities of bimetal interfacial content. Although they exhibit yield strengths approaching theoretical limits, multilayered materials with layer thicknesses less than 10. nm have shown limited ductility in rolling. In this study, bimodal 4. nm/40. nm Cu/Nb multilayers are rolled to 30% thickness reduction without the onset of shear instability. The stacking order used allows focus to be drawn specifically to the ductility by the boundary crossing mechanism exhibited in multilayered materials with layer thicknesses below 10. nm. Through the geometric constraint offered by alternating 4. nm and 40. nm layer thickness modes, the onset of localized shear is avoided and the 4. nm layers can be rolled to large strains.

Original languageEnglish (US)
Pages (from-to)213-217
Number of pages5
JournalMaterials Science and Engineering A
Volume564
DOIs
StatePublished - Mar 1 2013

Keywords

  • Composites
  • Electron microscopy
  • Interfaces
  • Nanoindentation
  • Nanostructured materials
  • Orientation relationships

Fingerprint

Dive into the research topics of 'Large strain deformation of bimodal layer thickness Cu/Nb nanolamellar composites'. Together they form a unique fingerprint.

Cite this