Three poly(styrene)-block-poly(isoprene)-block-poly-(lactide) (PS-b-PI-b-PLA, SIL) triblock terpolymers were synthesized and characterized in the bulk and as thin films. The pronounced incompatibility of the covalently connected PI and PLA led to significant frustration and the tendency to minimize their intermaterial dividing surface area. This resulted in the formation of a core-shell cylinder morphology with exaggerated nonconstant mean curvature from triblock polymers with equal block volume fractions rather than the more typical lamellar morphology. The effect of frustration was magnified in thin films by both confinement and interfacial interactions such that the PI domains became discontinuous. Self-consistent field theory (SCFT) calculations emphasize that the marked difference in the PS/PI and PI/PLA interaction parameters promotes the formation of nonlamellar morphologies. However, SCFT predicts that lamellar morphology is more stable than the observed cylindrical morphology, demonstrating a limitation that arises from the underlying assumptions.
Bibliographical noteFunding Information:
This work was supported by the National Science Foundation (DMR-1333669). M.R.R. holds the Camille and Henry Dreyfus Foundation Postdoctoral Fellowship in Environmental Chemistry. Y.A was financially supported by the Program for Leading Graduate Schools "Integrative Graduate Education and Research in Green Natural Sciences", MEXT, Japan. rac-Lactide was generously provided by Ortec. Parts of this work were carried out in the Characterization Facility, University of Minnesota, which receives partial support from NSF through the MRSEC program. SAXS data were obtained at the DuPont-Northwestern-Dow Collaborative Access Team (DND-CAT) located at Sector 5 of the Advanced Photon Source, a U.S. Department of Energy (DOE) Office of Science user facility operated for the DOE Office of Science by Argonne National Laboratory under Contract DE-AC02-06CH11357.
How much support was provided by MRSEC?
Reporting period for MRSEC
- Period 3