Phase segregation of poly(3-dodecylthiophene)-block-poly(methyl methacrylate) copolymers

Hong Chul Moon, Jin Kon Kim

Research output: Contribution to journalArticlepeer-review

16 Scopus citations

Abstract

We investigated, via small angle X-ray scattering (SAXS), the ordered-to-disordered transition temperature (TODT) of symmetric poly(3-dodecylthiophene)-block-poly(methyl methacrylate) copolymers (P3DDT-b-PMMA) with different molecular weights synthesized by anionic coupling reaction. When the molecular weight of P3DDT-b-PMMA was properly chosen, the TODT was observed within experimentally accessible temperature range (higher than the glass transition and melting temperature for PMMA and P3DDT, respectively, but lower than the thermal degradation temperature). We also measured the temperature dependence of Flory-Huggins interaction parameter (χ) between P3DDT and PMMA as χ = 0.1109 + 76.63/T, in which T is the absolute temperature.

Original languageEnglish (US)
Pages (from-to)5437-5442
Number of pages6
JournalPolymer
Volume54
Issue number20
DOIs
StatePublished - Sep 6 2013

Bibliographical note

Funding Information:
This work was supported by the National Creative Research Initiative Program supported by the National Research Foundation of Korea (NRF) . Small-angle X-ray scattering was performed at PLS beam line 9A and 4C supported by POSCO and KOSEF. We also thank Dr. Tae Joo Shin and Dr. Kyeong Sik Jin for helping SAXS experiment.

Copyright:
Copyright 2018 Elsevier B.V., All rights reserved.

Keywords

  • Ordered-to-disordered transition
  • Rigid rod-flexible block copolymer
  • Temperature dependence of interaction parameter

Fingerprint Dive into the research topics of 'Phase segregation of poly(3-dodecylthiophene)-block-poly(methyl methacrylate) copolymers'. Together they form a unique fingerprint.

Cite this