N2 - The fabrication and characterization of single-walled carbon nanotube (SWCNT) composite thin film micropatterns and suspended beams prepared by lithography-compatible layer-by-layer (LbL) nano-self-assembly are demonstrated. Negatively charged SWCNTs are assembled with a positively charged polydiallyldimethylammonium chloride, and the composite thin film is patterned by oxygen plasma etching with a masking layer of photoresist, resulting in a feature size of 2νm. Furthermore, the SWCNT nanocomposite stripe pattern with a metal clamp on both ends is released by etching a sacrificial layer of silicon dioxide in the hydrofluoric acid vapor. I-V measurement reveals that the resistance of SWCNT nanocomposite film decreases by 23% upon release, presumably due to the effect of reorientation of CNTs caused by the deflection of about 50nm. A high Young's modulus is found in a range of 500-800GPa based on the characterization of a fixed-fixed beam using nanoindentation. This value is much higher than those of the other CNT-polymer composites reported due to organization of structures by self-assembly and higher loading of CNTs. The stiff CNT-polymer composite thin film micropattern and suspended beam have potential applications to novel physical sensors, nanoelectromechanical switches, other M/NEMS devices, etc.
AB - The fabrication and characterization of single-walled carbon nanotube (SWCNT) composite thin film micropatterns and suspended beams prepared by lithography-compatible layer-by-layer (LbL) nano-self-assembly are demonstrated. Negatively charged SWCNTs are assembled with a positively charged polydiallyldimethylammonium chloride, and the composite thin film is patterned by oxygen plasma etching with a masking layer of photoresist, resulting in a feature size of 2νm. Furthermore, the SWCNT nanocomposite stripe pattern with a metal clamp on both ends is released by etching a sacrificial layer of silicon dioxide in the hydrofluoric acid vapor. I-V measurement reveals that the resistance of SWCNT nanocomposite film decreases by 23% upon release, presumably due to the effect of reorientation of CNTs caused by the deflection of about 50nm. A high Young's modulus is found in a range of 500-800GPa based on the characterization of a fixed-fixed beam using nanoindentation. This value is much higher than those of the other CNT-polymer composites reported due to organization of structures by self-assembly and higher loading of CNTs. The stiff CNT-polymer composite thin film micropattern and suspended beam have potential applications to novel physical sensors, nanoelectromechanical switches, other M/NEMS devices, etc.
UR - http://www.scopus.com/inward/record.url?scp=79952635892&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=79952635892&partnerID=8YFLogxK
U2 - 10.1088/0957-4484/22/16/165601
DO - 10.1088/0957-4484/22/16/165601
M3 - Article
C2 - 21393826
AN - SCOPUS:79952635892
SN - 0957-4484
VL - 22
JO - Nanotechnology
JF - Nanotechnology
IS - 16
M1 - 165601
ER -